Statistical Modelling of Ultrasonic Pulse Velocity of Fly Ash Based Geopolymer mortar using response surface methodology

Authors

  • Muhammad Zahid Department of Civil Engineering, Universiti Teknologi Petronas, Seri Iskandar,
  • Nasir Shafiq Department of Civil Engineering, Universiti Teknologi Petronas, Seri Iskandar
  • Muhammad Ali Department of Civil Engineering, University of Engineering and Technology Lahore

DOI:

https://doi.org/10.30564/jaeser.v2i4.1558

Abstract

The fly ash based geopolymer has emerged as a capable and sustainable binder material in construction industry. Ultrasonic pulse velocity (UPV) method is a non-destructive technique for investigating the mechanical performance of concrete. Experimental investigation was performed for studying the effect of NaOH Molarity, Na2SiO3/NaOH and curing temperature on the ultrasonic pulse velocity of geopolymer mortar. Experiments were designed based on central composite design (CCD) technique of response surface methodology (RSM). Statistical model was developed and statistically validated and found significant as the difference between adjustable R-squared and predicted R-squared less than 0.2. Finally, the optimized mix proportion was assessed for maximized value of UPV. Experimental validation on the optimized mix reveals the close agreement between experimental and predicted values of UPV with significance level of more than 95%. The proposed technique improves the yield, the reliability of the product and the processes.

Keywords:

Geopolymer;fly ash;NaOH molarity;Na2SiO3/NaOH;curing temperature; ultrasonic pulse velocity;response surface methodology;Optimization.

References

[1] P. D. United Nations, Department of Economic and Social Affairs, “World Population Prospects The 2017 Revision Key Findings and Advance Tables,” World Popul. Prospect. 2017, pp. 1–46, 2017.

[2] J. Wang, Y. Wang, Y. Sun, D. D. Tingley, and Y. Zhang, “Life cycle sustainability assessment of fly ash concrete structures,” Renew. Sustain. Energy Rev., vol. 80, no. August, pp. 1162–1174, 2017.

[3] Z. Liu, “China’s Carbon Emissions Report,” 2015.

[4] M. Zahid, N. Shafiq, and A. Jalal, “Investigating the effects of solarcure curing method on the compressive strength , microstructure and polymeric reaction of fly ash based geopolymer,” Constr. Build. Mater., vol. 181, pp. 227–237, 2018.

[5] J.Davidovits, “Geopolymers: inorganic polymeric new materials,” J. Therm. Anal., pp. 1633–1656, 1991.

[6] D. Hardjito and B. V. Rangan, “Development and properties of low-calcium fly ash-based geopolymer concrete,” Res. Rep. GC, p. 94, 2005.

[7] J. Davidovits, “PROPERTIES OF GEOPOLYMER CEMENTS Joseph Davidovits Geopolymer Institute, 02100 Saint-Quentin, France,” Alkaline Cem. Concr. KIEV Ukr., pp. 1–19, 1994.

[8] Z. Li, Z. Ding, Y. Zhang, C. W. Bay, and H. Kong, “DEVELOPMENT OF SUSTAINABLE CEMENTITIOUS,” Int. Work. Sustain. Dev. Concr. Technol., vol. 1, no. 1, pp. 55–76, 2004.

[9] T. Öztürk, O. Kroggel, P. Grübl, and J. S. Popovics, “Improved ultrasonic wave reflection technique to monitor the setting of cement-based materials,” NDT E Int., vol. 39, no. 4, pp. 258–263, 2006.

[10] I. A. E. A. IAEA, “Guidebook on non-destructive testing of concrete structures,” Train. Course Ser., vol. 17, no. 17, p. 231, 2002.

[11] Y. Yang, M. D. Lepech, E. H. Yang, and V. C. Li, “Autogenous healing of engineered cementitious composites under wet-dry cycles,” Cem. Concr. Res., vol. 39, no. 5, pp. 382–390, 2009.

[12] R. Ghosh, S. P. Sagar, A. Kumar, S. K. Gupta, and S. Kumar, “Estimation of geopolymer concrete strength from ultrasonic pulse velocity (UPV) using high power pulser,” J. Build. Eng., vol. 16, no. December 2017, pp. 39–44, 2018.

[13] Y. Cho, “Non-destructive testing of high strength concrete using spectral analysis of surface waves,” NDT E Int., vol. 36, no. 4, pp. 229–235, 2003.

[14] T. H. Panzera, A. L. Christoforo, F. P. Cota, P. H. R. Borges, and C. R. Bowen, “Ultrasonic Pulse Velocity Evaluation of Cementitious Materials,” Adv. Compos. Mater. - Anal. Nat. man-made Mater., vol. 17, pp. 411–436, 2011.

[15] T. U. Mohammed and M. N. Rahman, “Effect of types of aggregate and sand-to-aggregate volume ratio on UPV in concrete,” Constr. Build. Mater., vol. 125, pp. 832–841, 2016.

[16] Z. Lafhaj, M. Goueygou, A. Djerbi, and M. Kaczmarek, “Correlation between porosity, permeability and ultrasonic parameters of mortar with variable water / cement ratio and water content,” Cem. Concr. Res., vol. 36, no. 4, pp. 625–633, 2006.

[17] T. Mandal, J. M. Tinjum, and T. B. Edil, “Non-destructive testing of cementitiously stabilized materials using ultrasonic pulse velocity test,” Transp. Geotech., vol. 6, pp. 97–107, 2016.

[18] U. Lencis, A. Udris, and A. Korjakins, “Moisture effect on the ultrasonic pulse velocity in concrete cured under normal conditions and at elevated temperature,” Constr. Sci., no. 10.2478, p. 8, 2014.

[19] H. Güneyli, S. Karahan, A. Güneyli, and N. Yapιcι, “Water content and temperature effect on ultrasonic pulse velocity of concrete,” Russ. J. Nondestruct. Test., vol. 53, no. 2, pp. 159–166, 2017.

[20] W. Ren, J. Xu, and E. Bai, “Strength and Ultrasonic Characteristics of Alkali-Activated Fly Ash-Slag Geopolymer Concrete after Exposure to Elevated Temperatures,” J. Mater. Civ. Eng., vol. 28, no. 2, p. 04015124, 2016.

[21] W. C. Wang, H. Y. Wang, and M. H. Lo, “The fresh and engineering properties of alkali activated slag as a function of fly ash replacement and alkali concentration,” Constr. Build. Mater., vol. 84, pp. 224–229, 2015.

[22] B. Nematollahi, J. Sanjayan, and F. U. A. Shaikh, “Matrix design of strain hardening fiber reinforced engineered geopolymer composite,” Compos. Part B Eng., vol. 27, no. 10, pp. 253–265, 2015.

[23] ASTM C597, “Standard test method for Pulse Velocity Through Concrete,” Annu. B. ASTM Stand., no. Note 2, pp. 6–9, 2009.

[24] J. G. . van Jaarsveld et al., “The effect of composition and temperature on the properties of fly ash- and kaolinite-based geopolymers,” Chem. Eng. J., vol. 89, no. 1–3, pp. 63–73, 2002.

[25] P. Chindaprasirt, C. Jaturapitakkul, W. Chalee, and U. Rattanasak, “Comparative study on the characteristics of fly ash and bottom ash geopolymers,” Waste Manag., vol. 29, no. 2, pp. 539–543, 2009.

[26] N. Shafiq, R. Kumar, M. Zahid, and R. F. Tufail, “Effects of Modified Metakaolin Using Nano-Silica on the Mechanical Properties and Durability of Concrete,” Materials (Basel)., vol. 12, no. 14, p. 2291, 2019.

[27] X. Feng, R. Faisal, and M. Zahid, “Experimental Investigation and Statistical Modeling of FRP Confined RuC Using Response Surface Methodology,” Civ. Eng. J., vol. 5, no. 2, pp. 268–283, 2019.

[28] Zahid and L. G. Muhammad Zahid, Nasir Shafiq, M. Hasnain Isa, “Statistical modeling and mix design optimization of fly ash based engineered geopolymer composite using response surface methodology,” Clean. Prod., vol. 194, 2018.

Downloads

How to Cite

Zahid, M., Shafiq, N., & Ali, M. (2020). Statistical Modelling of Ultrasonic Pulse Velocity of Fly Ash Based Geopolymer mortar using response surface methodology. Journal of Architectural Environment & Structural Engineering Research, 2(4), 11–17. https://doi.org/10.30564/jaeser.v2i4.1558

Issue

Article Type

Article